Bead Wire
Brief introduction
As the important reinforcement of the tyres, made of steel and coated with copper, bead wire can strengthen the tyres.
Specification: We can offer bead wire from §¶ 0.89mm to §¶ 1.65mm.
Packing: Packed in reels, then put on pallets, using standard packing materials and methods. One 20-foot container can hold 20 metric tons.
Payment terms: L/C at sight or T/T.
Specification of Bead Wire:
Specification:§¶0.89
Diameter £¨ mm £© |
0.89¡À 0.02 mm |
Breaking Strenghth £¨ Kg/wire £© |
¡Ý115 |
Elongation(%) |
¡Ý5% |
Torsion(Turns/L=200D) |
¡Ý52 |
Straightness(mm/ 3m ) |
¡Ü 600 mm |
Bronze plate composition |
Copper(%) |
¡Ý97% |
Tin(%) |
¡Ü3.0% |
Plating thickness(g/kg) |
0.30-1.35 |
Adhesion force(N) |
¡Ý800N |
Tensile strength(Mpa) |
¡Ý1850 Mpa |
Steel Analysis |
C(%) |
0.65-0.90 |
Mn(%) |
0.30-0.80 |
Si(%) |
0.17-0.37 |
P&S(%) |
¡Ü0.030 |
Linear Density(g/m) |
4.90¡À0.1 |
Bend on 2.50mm (Min) |
11 |
Specification:§¶0.95
Diameter £¨ mm £© |
0.95¡À 0.02 mm |
Breaking Strenghth £¨ Kg/wire £© |
¡Ý136 |
Elongation(%) |
¡Ý5% |
Torsion(Turns/L=200D) |
¡Ý50 |
Straightness(mm/ 3m ) |
¡Ü 600 mm |
Bronze plate composition |
Copper(%) |
¡Ý97% |
Tin(%) |
¡Ü3.0% |
Plating thickness(g/kg) |
0.30-1.35 |
Adhesion force(N) |
¡Ý800N |
Tensile strength(Mpa) |
¡Ý1850 Mpa |
Steel Analysis |
C(%) |
0.65-0.90 |
Mn(%) |
0.30-0.80 |
Si(%) |
0.17-0.37 |
P&S(%) |
¡Ü0.030 |
Linear Density(g/m) |
5.65¡À0.2 |
Bend on 2.50mm (Min) |
11 |
Specification:§¶0.96
Diameter £¨ mm £© |
0.96¡À 0.02 mm |
Appearance Quality |
Appearance plating uniform and Qualified |
Tensile strength £¨ Mpa £© |
¡Ý1850 |
Breaking Strenghth £¨ Kg/wire £© |
¡Ý136 |
Elongation(%) |
¡Ý5% |
Torsion(Turns/L=200D) |
¡Ý50 |
Straightness(mm/ 3m ) |
¡Ü 600 mm |
Bronze plate composition |
Copper(%) |
¡Ý97% |
Tin(%) |
¡Ü3.0% |
Plating thickness(g/kg) |
0.30-1.35 |
Adhesion force(N) |
¡Ý800N |
Tensile strength(Mpa) |
¡Ý1850 Mpa |
Steel Analysis |
C(%) |
0.65-0.90 |
Mn(%) |
0.30-0.80 |
Si(%) |
0.17-0.37 |
P&S(%) |
¡Ü0.030 |
Linear Density(g/m) |
5.68¡À0.2 |
Bend on 2.50mm (Min) |
11 |
Specification:§¶1.0
Diameter £¨ mm £© |
1.0¡À 0.02 mm |
Breaking Strenghth £¨ Kg/wire £© |
¡Ý148 |
Elongation(%) |
¡Ý5% |
Torsion(Turns/L=200D) |
¡Ý52 |
Straightness(mm/ 3m ) |
¡Ü 600 mm |
Bronze plate composition |
Copper(%) |
¡Ý97% |
Tin(%) |
¡Ü3.0% |
Plating thickness(g/kg) |
0.30-1.35 |
Adhesion force(N) |
¡Ý800N |
Tensile strength(Mpa) |
¡Ý1850 Mpa |
Steel Analysis |
C(%) |
0.65-0.90 |
Mn(%) |
0.30-0.80 |
Si(%) |
0.17-0.37 |
P&S(%) |
¡Ü0.030 |
Linear Density(g/m) |
6.20¡À0.2 |
Bend on 2.50mm (Min) |
11 |
Specification:§¶1.65
Diameter £¨ mm £© |
1.65¡À 0.03 mm |
Breaking Strenghth £¨ Kg/wire £© |
¡Ý375 |
Elongation(%) |
¡Ý5% |
Torsion(Turns/L=200D) |
¡Ý40 |
Straightness(mm/ 3m ) |
¡Ü 600 mm |
Bronze plate composition |
Copper(%) |
¡Ý97% |
Tin(%) |
¡Ü3.0% |
Plating thickness(g/kg) |
0.30-1.35 |
Adhesion force(N) |
¡Ý800N |
Tensile strength(Mpa) |
¡Ý1770Mpa |
Steel Analysis |
C(%) |
0.65-0.90 |
Mn(%) |
0.30-0.80 |
Si(%) |
0.17-0.37 |
P&S(%) |
¡Ü0.030 |
Linear Density(g/m) |
16.8¡À0.4 |
Bend on 2.50mm (Min) |
10 |
Note: All the above products can be produced as customers' requirement.